Inconel 600 is a nickel-chromium-iron alloy designed for applications requiring high strength and excellent corrosion resistance at both room and elevated temperatures. It offers outstanding resistance to oxidation, carburization, and chloride-induced stress corrosion cracking, and remains stable in a wide range of corrosive environments, including acids, alkalis, and high-temperature gases. With good formability and weldability, it is widely used in chemical processing, heat treatment equipment

Advantage

1. Excellent resistance to oxidation and carburization at high temperatures 2. Superior resistance to chloride-induced stress corrosion cracking 3. Good formability and weldability, suitable for various processing methods

Ingredient

• C
• ≤0.15
• Si
• ≤0.50
• Mn
• ≤1.00
• S
• ≤0.015
• Ni
• ＞72
• Cu
• ≤0.50
• Fe
• 6.0-10.0
• Cr
• 14.0-17.0
• Co
• ≤1.00

Standard

• USA
• ASTM B166 / ASME SB166
• CN
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Annealed
• ≥655 MPa
• ≥240 MPa
• ≥240 MPa
• ≥35 %
• ≤195 HBW
• ≥27 J
• Solution Annealed
• ≥640 MPa
• ≥235 MPa
• ≥35 %
• ≥35 %
• ≤195 HBW
• ≥27 J

• STATE
• Solution Annealed
• RP
• ≥655 MPa
• YIELD
• ≥240 MPa
• EXTEND
• ≥240 MPa
• SHRINK
• ≥35 %
• HARDNESS
• ≤195 HBW
• IMPACT
• ≥27 J
• STATE
• Solution Annealed
• RP
• ≥640 MPa
• YIELD
• ≥235 MPa
• EXTEND
• ≥35 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤195 HBW
• IMPACT
• ≥27 J