Inconel600
Nickel Alloys
Inconel 600 is a nickel-chromium-iron alloy designed for applications requiring high strength and excellent corrosion resistance at both room and elevated temperatures. It offers outstanding resistance to oxidation, carburization, and chloride-induced stress corrosion cracking, and remains stable in a wide range of corrosive environments, including acids, alkalis, and high-temperature gases. With good formability and weldability, it is widely used in chemical processing, heat treatment equipment
Advantage
1. Excellent resistance to oxidation and carburization at high temperatures 2. Superior resistance to chloride-induced stress corrosion cracking 3. Good formability and weldability, suitable for various processing methods
Ingredient
- C
- ≤0.15
- Si
- ≤0.50
- Mn
- ≤1.00
- S
- ≤0.015
- Ni
- ＞72
- Cu
- ≤0.50
- Fe
- 6.0-10.0
- Cr
- 14.0-17.0
- Co
- ≤1.00
- Board
- Stick
- Pipe
- Forging
Title
Inconel 600 Board
Size
0.5mm - 80mmLength
1000mm - 6000mm (customizable)Production
Hot rolled + Solution annealingSurface
Pickled / 2B / PolishedProcessing
Hot rolled + Solution annealingStandard
- USA
- ASTM B168 / ASME SB168
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥655 MPa
- ≥240 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- Solution Annealed
- ≥640 MPa
- ≥235 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥655 MPa
- YIELD
- ≥240 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥640 MPa
- YIELD
- ≥235 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
Title
Inconel600 stick
Size
Φ3mm - Φ300mmLength
1000mm - 6000mm (customizable)Production
1000mm - 6000mm (customizable)Surface
Black skin / Turned / PolishedProcessing
1000mm - 6000mm (customizable)Standard
- USA
- ASTM B166 / ASME SB166
- CN
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥655 MPa
- ≥240 MPa
- ≥240 MPa
- ≥35 %
- ≤195 HBW
- ≥27 J
- Solution Annealed
- ≥640 MPa
- ≥235 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥655 MPa
- YIELD
- ≥240 MPa
- EXTEND
- ≥240 MPa
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥640 MPa
- YIELD
- ≥235 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
Title
Inconel 600 Pipe
Size
Φ6mm - Φ325mmLength
1000mm - 6000mm (customizable)Production
Hot extruded + Cold drawn + Solution annealingSurface
Pickled / Bright annealedProcessing
Hot extruded + Cold drawn + Solution annealingStandard
- USA
- ASTM B167 / ASME SB167
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥655 MPa
- ≥240 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- Solution Annealed
- ≥640 MPa
- ≥235 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥655 MPa
- YIELD
- ≥240 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥640 MPa
- YIELD
- ≥235 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
Title
Inconel 600 Forging
Size
Custom customizedLength
Custom customizableProduction
Hot forging + Solution annealingSurface
Forged black surface / Rough machining / Finish machiningProcessing
Hot forging + Solution annealingStandard
- USA
- ASTM B564 / ASME SB564
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed (per ASTM B564)
- ≥655 MPa
- ≥240 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- Solution Annealed (per GB/T 15007)
- ≥640 MPa
- ≥235 MPa
- ≥35 %
- ≥35 %
- ≤195 HBW
- ≥27 J
- STATE
- Solution Annealed (per ASTM B564)
- RP
- ≥655 MPa
- YIELD
- ≥240 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed (per GB/T 15007)
- RP
- ≥640 MPa
- YIELD
- ≥235 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥35 %
- HARDNESS
- ≤195 HBW
- IMPACT
- ≥27 J