Inconel 601 is a nickel-chromium-iron alloy with outstanding resistance to high-temperature oxidation, carburization, and other forms of high-temperature corrosion. Its high aluminum content forms a dense, adherent oxide scale that provides excellent protection against oxidation even at temperatures up to 1200°C. The alloy also offers good mechanical strength, creep resistance, and resistance to chloride stress corrosion cracking, making it ideal for furnace components, heat treatment equipment,

Advantage

1. Exceptional resistance to high-temperature oxidation up to 1200°C 2. Good resistance to carburization and sulfidation in high-temperature environments 3. High mechanical strength and creep resistance at elevated temperatures 4. Reliable resistance to chloride-induced stress corrosion cracking

Ingredient

• C
• ≤0.10
• Si
• ≤0.50
• Mn
• ≤1.00
• Cr
• 21.0-25.0
• S
• ≤0.015
• Ni
• 58.0-63.0 (Balance)
• Cu
• ≤1.00
• Fe
• 10.0-15.0
• Co
• ≤1.00
• Al
• 1.0-1.7

• Board
• Stick
• Pipe
• Forging

Title

Inconel601board

Size

0.5mm - 80mm

Length

1000mm - 6000mm (customizable)

Production

Hot rolled + Solution annealing

Surface

Pickled / Polished / 2B

Processing

Hot rolled + Solution annealing

Standard

• USA
• ASTM B168 / ASME SB168
• China
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Annealed
• ≥655 MPa
• ≥345 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J
• Solution Annealed
• ≥640 MPa
• ≥335 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J

• STATE
• Solution Annealed
• RP
• ≥655 MPa
• YIELD
• ≥345 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J
• STATE
• Solution Annealed
• RP
• ≥640 MPa
• YIELD
• ≥335 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J

Title

Inconel 601 Stick

Size

Φ3mm - Φ300mm

Length

1000mm - 6000mm (customizable)

Production

Forging + Solution annealing

Surface

Black skin / Polished / Turned

Processing

Forging + Solution annealing

Standard

• USA
• ASTM B166 / ASME SB166
• China
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Annealed
• ≥655 MPa
• ≥345 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J
• Solution Annealed
• ≥640 MPa
• ≥335 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J

• STATE
• Solution Annealed
• RP
• ≥655 MPa
• YIELD
• ≥345 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J
• STATE
• Solution Annealed
• RP
• ≥640 MPa
• YIELD
• ≥335 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J

Title

Inconel 601 Pipe

Size

Φ6mm - Φ325mm

Length

1000mm - 6000mm (customizable)

Production

Hot extruded / Cold drawn + Solution annealing

Surface

Pickled / Bright annealed / Polished

Processing

Hot extruded / Cold drawn + Solution annealing

Standard

• USA
• ASTM B167 / ASME SB167
• China
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Annealed
• ≥655 MPa
• ≥345 MPa
• ≥30 %
• ≥35 %
• ≥35 %
• ≥27 J
• Solution Annealed
• ≥640 MPa
• ≥335 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J

• STATE
• Solution Annealed
• RP
• ≥655 MPa
• YIELD
• ≥345 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≥35 %
• IMPACT
• ≥27 J
• STATE
• Solution Annealed
• RP
• ≥640 MPa
• YIELD
• ≥335 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J

Title

Inconel 601 Forging

Size

Custom customized

Length

Custom customizable

Production

Hot forging + Solution annealing

Surface

Forged black surface / Machined

Processing

Hot forging + Solution annealing

Standard

• USA
• ASTM B564 / ASME SB564
• China
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Annealed
• ≥655 MPa
• ≥345 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J
• Solution Annealed
• ≥640 MPa
• ≥335 MPa
• ≥30 %
• ≥35 %
• ≤210 HBW
• ≥27 J

• STATE
• Solution Annealed
• RP
• ≥655 MPa
• YIELD
• ≥345 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J
• STATE
• Solution Annealed
• RP
• ≥640 MPa
• YIELD
• ≥335 MPa
• EXTEND
• ≥30 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤210 HBW
• IMPACT
• ≥27 J