316L is a low-carbon molybdenum-bearing austenitic stainless steel. The addition of molybdenum greatly enhances its resistance to pitting, crevice corrosion and chloride corrosion. With excellent oxidation resistance, good ductility, weldability and cold working performance, it can effectively avoid intergranular corrosion. It is widely used in chemical processing, marine equipment, food machinery, medical devices and general industrial corrosion-resistant components.

Advantage

1.Molybdenum alloyed design provides outstanding chloride and salt corrosion resistance 2.Ultra-low carbon content prevents intergranular corrosion after welding 3.Excellent toughness, formability and stable mechanical properties at various temperatures 4.Good wear resistance and comprehensive cost performance for universal industrial applications

Ingredient

• Cr
• 16.00 ~ 18.50
• Ni
• 10.00 ~ 14.00
• Mo
• 2.00 ~ 3.00
• C
• ≤0.03
• Mn
• ≤2.00
• Si
• ≤1.00
• P
• ≤0.045
• S
• ≤0.030
• Fe
• Balance

• Board
• Stick
• Pipe
• Forging

Title

316L Board

Size

0.5mm – 100mm

Length

1000mm – 6000mm (customizable)

Production

Hot rolled + Annealed

Surface

Pickled / 2B / Polished

Processing

Hot rolled + Annealed

Standard

• USA
• ASTM A240 / ASME SA240
• China
• GB/T 3280‑2015、GB/T 4237‑2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Annealed
• ≥485 MPa
• ≥170 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J
• Annealed
• ≥450 MPa
• ≥160 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J

• STATE
• Annealed
• RP
• ≥485 MPa
• YIELD
• ≥170 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J
• STATE
• Annealed
• RP
• ≥450 MPa
• YIELD
• ≥160 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J

Title

316L Stick

Size

8mm – 300mm

Length

1000mm – 6000mm (customizable)

Production

Hot rolled + Annealed

Surface

Black / Peeled / Polished

Processing

Hot rolled + Annealed

Standard

• USA
• ASTM A276 / ASME SA479
• China
• GB/T 1220‑2021、GB/T 4356‑2021

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Annealed
• ≥485 MPa
• ≥170 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J
• Annealed
• ≥450 MPa
• ≥160 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J

• STATE
• Annealed
• RP
• ≥485 MPa
• YIELD
• ≥170 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J
• STATE
• Annealed
• RP
• ≥450 MPa
• YIELD
• ≥160 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J

Title

316L Pipe

Size

6mm – 500mm OD, 1mm – 50mm WT

Length

1000mm – 12000mm (customizable)

Production

Hot finished + Annealed / Cold drawn + Annealed

Surface

Pickled / Bright annealed / Polished

Processing

Hot finished + Annealed / Cold drawn + Annealed

Standard

• USA
• ASTM A312 / ASME SA312
• China
• GB/T 12771‑2020、GB/T 14976‑2012

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Annealed
• ≥485 MPa
• ≥170 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J
• Annealed
• ≥450 MPa
• ≥170 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J

• STATE
• Annealed
• RP
• ≥485 MPa
• YIELD
• ≥170 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J
• STATE
• Annealed
• RP
• ≥450 MPa
• YIELD
• ≥170 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J

Title

316L Forging

Size

Custom size available

Length

Custom size available

Production

Forged + Annealed

Surface

Rough forged / Machined / Polished

Processing

Forged + Annealed

Standard

• USA
• ASTM A182 / ASME SA182
• China
• GB/T 4238‑2022、GB/T 10088‑2018

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Annealed
• ≥485 MPa
• ≥170 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J
• Annealed
• ≥450 MPa
• ≥160 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J

• STATE
• Annealed
• RP
• ≥485 MPa
• YIELD
• ≥170 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J
• STATE
• Annealed
• RP
• ≥450 MPa
• YIELD
• ≥160 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J