Monel400
Nickel Alloys
Monel 400 is a high-strength nickel-copper solid solution alloy with excellent corrosion resistance in alkaline, saltwater and mild acid environments. It features stable mechanical properties from low to moderate temperatures, good ductility and excellent weldability. The alloy performs exceptionally well in marine atmosphere, seawater, brine and chemical processing media, and is widely used in marine engineering, valve fittings, pump parts, heat exchangers and marine pipeline systems.
Advantage
1.Excellent seawater and marine atmospheric corrosion resistance 2.High mechanical strength and good toughness at normal and low temperatures 3.Fine resistance to alkali, salt solution and non-oxidizing acid corrosion 4.Superior processability, weldability and long service life in harsh working conditions
Ingredient
- Ni
- 63.0 ~ 70.0
- Cu
- Balance 28.0~34.0
- Fe
- ≤2.50
- Mn
- ≤2.00
- C
- ≤0.30
- Si
- ≤0.50
- S
- ≤0.024
- Board
- Stick
- Pipe
- Forging
Title
Hastelloy C22 Board
Size
0.5mm - 80mmLength
1000mm - 6000mm (customizable)Production
Hot rolled + Solution annealingSurface
Pickled / 2B / PolishedProcessing
Hot rolled + Solution annealingStandard
- USA
- ASTM B575 / ASME SB575
- C
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥690 MPa
- ≥283 MPa
- ≥40 %
- ≥45 %
- ≤100 HRB
- ≥27 J
- Solution Annealed
- ≥680 MPa
- ≥280 MPa
- ≥40 %
- ≥45 %
- ≤100 HRB
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥690 MPa
- YIELD
- ≥283 MPa
- EXTEND
- ≥40 %
- SHRINK
- ≥45 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥680 MPa
- YIELD
- ≥280 MPa
- EXTEND
- ≥40 %
- SHRINK
- ≥45 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
Title
Hastelloy C22 Stick
Size
Φ3mm - Φ300mmLength
1000mm - 6000mm (customizable)Production
Forging + Solution annealingSurface
Black skin / Turned / PolishedProcessing
Forging + Solution annealingStandard
- USA
- ASTM B574 / ASME SB574
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥690 MPa
- ≥283 MPa
- ≥40 %
- ≥50 %
- ≤100 HRB
- ≥27 J
- Solution Annealed
- ≥680 MPa
- ≥280 MPa
- ≥40 %
- ≥50 %
- ≤100 HRB
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥690 MPa
- YIELD
- ≥283 MPa
- EXTEND
- ≥40 %
- SHRINK
- ≥50 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥680 MPa
- YIELD
- ≥280 MPa
- EXTEND
- ≥40 %
- SHRINK
- ≥50 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
Title
Hastelloy C22 Pipe
Size
Φ6mm - Φ325mmLength
1000mm - 6000mm (customizable)Production
Hot extruded / Cold drawn + Solution annealingSurface
Pickled / Bright annealedProcessing
Hot extruded / Cold drawn + Solution annealingStandard
- USA
- ASTM B622 / ASME SB622
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥690 MPa
- ≥690 MPa
- ≥40 %
- ≥45 %
- ≤100 HRB
- ≥27 J
- Solution Annealed
- ≥680 MPa
- ≥280 MPa
- ≥40 %
- ≥45 %
- ≤100 HRB
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥690 MPa
- YIELD
- ≥690 MPa
- EXTEND
- ≥40 %
- SHRINK
- ≥45 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥680 MPa
- YIELD
- ≥280 MPa
- EXTEND
- ≥40 %
- SHRINK
- ≥45 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
Title
Hastelloy C22 Forging
Size
Custom customizedLength
Custom customizableProduction
Hot forging + Solution annealingSurface
Forged black surface / MachinedProcessing
Hot forging + Solution annealingStandard
- USA
- ASTM B564 / ASME SB564
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed
- ≥690 MPa
- ≥283 MPa
- ≥35 %
- ≥45 %
- ≤100 HRB
- ≥27 J
- Solution Annealed
- ≥680 MPa
- ≥280 MPa
- ≥35 %
- ≥45 %
- ≤100 HRB
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥690 MPa
- YIELD
- ≥283 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥45 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J
- STATE
- Solution Annealed
- RP
- ≥680 MPa
- YIELD
- ≥280 MPa
- EXTEND
- ≥35 %
- SHRINK
- ≥45 %
- HARDNESS
- ≤100 HRB
- IMPACT
- ≥27 J