Inconel625
Nickel Alloys
Inconel 625 is a nickel-chromium-molybdenum-niobium alloy known for its outstanding corrosion resistance and high-temperature strength. It exhibits excellent resistance to pitting, crevice corrosion, and stress corrosion cracking in a wide range of corrosive environments, including seawater and acidic media. With good fabricability and weldability, it is widely used in chemical processing, aerospace, marine engineering, and power generation industries.
Advantage
1.Excellent resistance to a wide range of corrosive environments, including seawater and acids 2. High strength and good creep-rupture properties at elevated temperatures 3. Good fabricability and weldability, suitable for complex processing
Ingredient
- C
- ≤0.10
- Si
- ≤0.50
- Mn
- ≤0.50
- P
- ≤0.015
- S
- ≤0.015
- Ni
- 58.0~63.0
- Fe
- ≤5.0
- Co
- ≤1.0
- Ti
- ≤0.40
- Al
- ≤0.40
- Nb+Ta
- 3.15 ~ 4.15
- Mo
- 8.0 ~ 10.0
- Cr
- 20.0 ~ 23.0
- Board
- Stick
- Pipe
- Forging
Title
Inconel625 board
Size
0.5mm - 80mmLength
1000mm - 6000mm (customizable)Production
Hot rolled + Solution annealingSurface
Pickled / Polished / 2BProcessing
Hot rolled + Solution annealingStandard
- USA
- ASTM B443 / ASME SB443
- China
- GB/T 15007-2017、GB/T 14992-2008
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed (per ASTM B443)
- ≥827 MPa
- ≥414 MPa
- ≥30 %
- ≥30 %
- ≤220 HBW
- ≥27 J
- Solution Annealed (per GB/T 15007)
- ≥800 MPa
- ≥400 MPa
- ≥30 %
- ≥30 %
- ≤220 HBW
- ≥27 J
- STATE
- Solution Annealed (per ASTM B443)
- RP
- ≥827 MPa
- YIELD
- ≥414 MPa
- EXTEND
- ≥30 %
- SHRINK
- ≥30 %
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed (per GB/T 15007)
- RP
- ≥800 MPa
- YIELD
- ≥400 MPa
- EXTEND
- ≥30 %
- SHRINK
- ≥30 %
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
Title
Inconel 625 Stick
Size
Φ3mm - Φ300mmLength
1000mm - 6000mm (customizable)Production
Forging + Solution annealingSurface
Black skin / Polished / TurnedProcessing
Forging + Solution annealingStandard
- USA
- ASTM B446 / ASME SB446
- China
- GB/T 15007-2017、GB/T 14992-2008
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed (per ASTM B446)
- ≥827 MPa
- ≥414 MPa
- ≥30 %
- ≥30 %
- ≤220 HBW
- ≥27 J
- Solution Annealed (per GB/T 15007)
- ≥800 MPa
- ≥400 MPa
- ≥30 %
- ≥30 %
- ≤220 HBW
- ≥27 J
- STATE
- Solution Annealed (per ASTM B446)
- RP
- ≥827 MPa
- YIELD
- ≥414 MPa
- EXTEND
- ≥30 %
- SHRINK
- ≥30 %
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed (per GB/T 15007)
- RP
- ≥800 MPa
- YIELD
- ≥400 MPa
- EXTEND
- ≥30 %
- SHRINK
- ≥30 %
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
Title
Inconel 625 Pipe
Size
Φ6mm - Φ325mmLength
Φ6mm - Φ325mmProduction
Hot extruded / Cold drawn + Solution annealingSurface
Pickled / Polished / Bright annealedProcessing
Hot extruded / Cold drawn + Solution annealingStandard
- USA
- ASTM B704 / ASME SB704
- China
- GB/T 15007-2017、GB/T 14992-2008
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed (per ASTM B704)
- ≥827 MPa
- ≥414 MPa
- ≥30 %
- ≥30 %
- ≤220 HBW
- ≥27 J
- Solution Annealed (per GB/T 15007)
- ≥800 MPa
- ≥400 MPa
- ≥30 %
- ≥30 %
- ≤220 HBW
- ≥27 J
- STATE
- Solution Annealed (per ASTM B704)
- RP
- ≥827 MPa
- YIELD
- ≥414 MPa
- EXTEND
- ≥30 %
- SHRINK
- ≥30 %
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed (per GB/T 15007)
- RP
- ≥800 MPa
- YIELD
- ≥400 MPa
- EXTEND
- ≥30 %
- SHRINK
- ≥30 %
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
Title
Inconel 625 Forging
Size
Custom customizedLength
Custom customizedProduction
Hot forging + Solution annealingSurface
Forged black surface / MachinedProcessing
Hot forging + Solution annealingStandard
- USA
- ASTM B564 / ASME SB564
- China
- GB/T 14992-2008、GB/T 15007-2017
Mechanics
- STATE
- RP
- YIELD
- EXTEND
- SHRINK
- HARDNESS
- IMPACT
- Solution Annealed（ASTM B564）
- ≥827 MPa
- ≥414 MPa
- ≥30%
- ≥30%
- ≤220 HBW
- ≥27 J
- Solution Annealed（GB/T 15007）
- ≥800 MPa
- ≥400 MPa
- ≥30%
- ≥30%
- ≤220 HBW
- ≥27 J
- STATE
- Solution Annealed（ASTM B564）
- RP
- ≥827 MPa
- YIELD
- ≥414 MPa
- EXTEND
- ≥30%
- SHRINK
- ≥30%
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J
- STATE
- Solution Annealed（GB/T 15007）
- RP
- ≥800 MPa
- YIELD
- ≥400 MPa
- EXTEND
- ≥30%
- SHRINK
- ≥30%
- HARDNESS
- ≤220 HBW
- IMPACT
- ≥27 J