Inconel 600 is a nickel-chromium-iron alloy designed for applications requiring high strength and excellent corrosion resistance at both room and elevated temperatures. It offers outstanding resistance to oxidation, carburization, and chloride-induced stress corrosion cracking, and remains stable in a wide range of corrosive environments, including acids, alkalis, and high-temperature gases. With good formability and weldability, it is widely used in chemical processing, heat treatment equipment

Advantage

1. Excellent resistance to oxidation and carburization at high temperatures 2. Superior resistance to chloride-induced stress corrosion cracking 3. Good formability and weldability, suitable for various processing methods

Ingredient

• C
• ≤0.15
• Si
• ≤0.50
• Mn
• ≤1.00
• S
• ≤0.015
• Ni
• ＞72
• Cu
• ≤0.50
• Fe
• 6.0-10.0
• Cr
• 14.0-17.0
• Co
• ≤1.00

Standard

• USA
• ASTM B564 / ASME SB564
• China
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Annealed (per ASTM B564)
• ≥655 MPa
• ≥240 MPa
• ≥35 %
• ≥35 %
• ≤195 HBW
• ≥27 J
• Solution Annealed (per GB/T 15007)
• ≥640 MPa
• ≥235 MPa
• ≥35 %
• ≥35 %
• ≤195 HBW
• ≥27 J

• STATE
• Solution Annealed (per ASTM B564)
• RP
• ≥655 MPa
• YIELD
• ≥240 MPa
• EXTEND
• ≥35 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤195 HBW
• IMPACT
• ≥27 J
• STATE
• Solution Annealed (per GB/T 15007)
• RP
• ≥640 MPa
• YIELD
• ≥235 MPa
• EXTEND
• ≥35 %
• SHRINK
• ≥35 %
• HARDNESS
• ≤195 HBW
• IMPACT
• ≥27 J