Inconel X750 is a precipitation-hardenable nickel-chromium alloy, strengthened by aluminum, titanium and niobium to form γ' phase [Ni₃(Al,Ti,Nb)]. It delivers high tensile strength, creep-rupture strength and excellent stress relaxation resistance at elevated temperatures, while maintaining good oxidation and corrosion resistance. Suitable for high-temperature springs, bolts, turbine components and nuclear parts operating from cryogenic to 870°C.

Advantage

1. High strength & creep resistance up to 870°C (1600°F) via γ' precipitation hardening 2.Excellent stress relaxation resistance, ideal for high-temperature springs and fasteners 3. Superior oxidation resistance up to 980°C (1800°F) and chloride stress corrosion cracking resistance 4. Good mechanical properties at cryogenic temperatures, reliable in extreme low-temperature environments

Ingredient

• C
• ≤0.08
• Si
• ≤0.50
• Mn
• ≤1.00
• Cr
• 14.0-17.0
• S
• ≤0.015
• Ni
• ≥70.0 (Balance)
• Cu
• ≤0.50
• Fe
• 5.0-9.0
• Ti
• 2.25-2.75
• Al
• 0.40-1.00
• Nb+Ta
• 0.70-1.20
• Co
• ≤1.00

Standard

• USA
• ASTM B564 / ASME SB564
• China
• GB/T 14992-2008、GB/T 15007-2017

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Solution Treated & Aged
• ≥1035 MPa
• ≥760 MPa
• ≥20%
• ≥25%
• HRC 32–40
• ≥27 J
• Solution Treated & Aged
• ≥1000 MPa
• ≥750 MPa
• ≥20%
• ≥25%
• 330–390 HBW
• ≥27 J

• STATE
• Solution Treated & Aged
• RP
• ≥1035 MPa
• YIELD
• ≥760 MPa
• EXTEND
• ≥20%
• SHRINK
• ≥25%
• HARDNESS
• HRC 32–40
• IMPACT
• ≥27 J
• STATE
• Solution Treated & Aged
• RP
• ≥1000 MPa
• YIELD
• ≥750 MPa
• EXTEND
• ≥20%
• SHRINK
• ≥25%
• HARDNESS
• 330–390 HBW
• IMPACT
• ≥27 J