316L is a low-carbon molybdenum-bearing austenitic stainless steel. The addition of molybdenum greatly enhances its resistance to pitting, crevice corrosion and chloride corrosion. With excellent oxidation resistance, good ductility, weldability and cold working performance, it can effectively avoid intergranular corrosion. It is widely used in chemical processing, marine equipment, food machinery, medical devices and general industrial corrosion-resistant components.

Advantage

1.Molybdenum alloyed design provides outstanding chloride and salt corrosion resistance 2.Ultra-low carbon content prevents intergranular corrosion after welding 3.Excellent toughness, formability and stable mechanical properties at various temperatures 4.Good wear resistance and comprehensive cost performance for universal industrial applications

Ingredient

• Cr
• 16.00 ~ 18.50
• Ni
• 10.00 ~ 14.00
• Mo
• 2.00 ~ 3.00
• C
• ≤0.03
• Mn
• ≤2.00
• Si
• ≤1.00
• P
• ≤0.045
• S
• ≤0.030
• Fe
• Balance

Standard

• USA
• ASTM A182 / ASME SA182
• China
• GB/T 4238‑2022、GB/T 10088‑2018

Mechanics

• STATE
• RP
• YIELD
• EXTEND
• SHRINK
• HARDNESS
• IMPACT
• Annealed
• ≥485 MPa
• ≥170 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J
• Annealed
• ≥450 MPa
• ≥160 MPa
• ≥40 %
• ≥40 %
• ≤217 HBW
• ≥27 J

• STATE
• Annealed
• RP
• ≥485 MPa
• YIELD
• ≥170 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J
• STATE
• Annealed
• RP
• ≥450 MPa
• YIELD
• ≥160 MPa
• EXTEND
• ≥40 %
• SHRINK
• ≥40 %
• HARDNESS
• ≤217 HBW
• IMPACT
• ≥27 J